Very recently, we succeede in preparing the low-loss and high-bandwirth graded-index plastic optical fiber (GI POF) from visible to near-infrared region. This paper reviews the updated high speed data transmission performance of the GI POF.

The recent study on the LCD backlight has been more important to achieve lower energy consumption for portable computers. It was thought that transparent polymer materials were nessesary for optical-transmission media. Therefore, for conventional edge-light type backlight system, it has been believed that a transparent PMMA homopolymer plate as a light pipe has been indispensable. However, this conventional system has not given satisfied luminance. In this paper, a bright LCD backlight with 2.5-12.1 inches using the highly scattering optical-transmission (HSOT) polymre is proposed.

シンプルで低コストな製造技術で新規ポリマー光デバイスを作製したので報告した。

近赤外領域（波長１.３μｍ）でのPOFを用いた高速伝送の報告である。材料として全フッ素化ポリマーを用い、屈折率分布型ポリマー光ファイバーを作製した。伝送損失値は波長１.３μｍにおいて約50dB/kmであり、理論的に10Gb/sの伝送速度で伝送が可能であることを明らかにした。

Recentry, information services which can be represented by the Internet service have become available to the general households, and a broaeband access network has been demanded to deliver video services with low cost and easy handling. In this paper, we propose a broadband graded-index type polymer optical fiber (GI-POF) for using an access network system. In the case of GI-POF, coupling loss caused by slight amount of displacement such as 30 micro meter is negligible because of the large core diameter.

光ファイバー光学素子の材料としてのポリマー材料に付き解説した。

The status of the polymer optical fiber (POF) for high-speed data communication is reviewed. Very recentry, the low-loss and high-bandwidth perfluorinated GI POF which has no serious absorption loss from visible to 1.3-µm wavelength was successfully prepared at Keio University. Since the core diameter (300-1000µm) of GI POF is much larger than that of the multimode silica fiber (62.5 µm),the serious modal noise in the conventional multimode silica fiber was virtually eliminated, resulting in stable giga bit order data transmission with inexpensive couples and connections.

Perfluorinated graded-index (GI) polymer optical fiber (POF) for near IR region was successfully prepared. The attenuation at 1.3 µm wavelength which is used for silica fiber is less than 60dB/km, while the attenuation of PMMA based GI POF at 1.3 µm wavelength is more than fifty thousand dB/km. Both model and material dispersion of perfluorinated GI POF were theoretically and experimentally confirmed. We propose a new concept of using the GI POF having giga bps transmission for the last one mile of the Information Superhighway.

様々なポリマー光ファイバーの応用とその原理を解説した。

マルチメディアネットワークをターゲットにした屈折率分布型ポリマー光ファイバーの高速伝送特性を解説した。

マルチメディアネットワークをターゲットにした屈折率分布型ポリマー光ファイバーの構造と特性を解説した。

屈折率分布型ポリマー光ファイバーと、これに光増幅機能を持たせたポリマー光ファイバー増幅器の最新の特性を報告した。

21世紀マルチメディア情報社会を支えるためのポリマー材料の可能性に付き探った。

高速情報通信社会（マルチメディア社会）で用いることの可能な屈折率分布型ポリマー光ファイバーの特性について報告した。

広帯域ＧＩ型ＰＯＦおよび高出力ＧＩ型ＰＯＦアンプの基本特性に付き、解説した。

マルチメディアネットワークをターゲットにした屈折率分布型ポリマー光ファイバーの構造と特性を解説した。

高伝送帯域を有する屈折率分布型ポリマー光ファイバーの実用化へ向けた特性を報告した。

新しい光媒体として光の導波と拡散出射の二つの働きを併せもつ新しい照明用導光体である光散乱ポリマー導光体について、その内部での光挙動に関する検討、及びその液晶用高輝度バックライトへの応用例を述べる。

屈折率分布制御によって初めて達成される新しい機能性光学ファイバーに焦点を絞り、従来の屈折率均一材料と比較しつつ解説する。

新しい光媒体として光の導波と拡散出射の二つの働きを併せもつ新しい照明用導光体である光散乱ポリマー導光体についてその内部での光の挙動に関する検討及びその液晶用高輝度バックライトへの応用例を述べた。