リパーゼを用いたグリーン・サステイナブルポリマーの合成についてまとめた。

The lipase-catalyzed degradation of poly(butylene adipate) (PBA) and poly(butylene succinate) (PBS) into cyclic oligomers and their polymerizability were analyzed. The enzymatic polymerization of a cyclic oligomer was dependent on its ring-size. The highest molecular weight PBA with an Mw of 173000 was produced by the polymerization of the cyclic BA monomer The molecular weight decreased to around Mw 60000 by polymerization of the cyclic BA dimer and trimer. Similar results were obtained for PBS. For the efficient chemical recycling of PBA and PBS, the cyclic BA monomer and the cyclic BS dimer had the best oligomer sizes, respectively. As an application of the enzymatic degradation for the chemical recycling of PBS, the selective recycling of the PBS/poly(L-lactic acid)(PLLA) polymer blend was carried out using a lipase and a clay catalyst, montmorillonite K5.

酵素触媒重合による環境低負荷型高分子合成とケミカルリサイクルについてまとめた。

グリーンポリウレタンの分子設計を行うに当たって必要とされるグリーンポリマーケミストリー、ポリウレタンの生分解性及びリサイクル法について概要を紹介したあと、ポリウレタンの従来型合成法、環境を意識したポリウレタンの新製法を記し、最後に著者らの酵素法によるグリーンポリウレタン創成について紹介した

生分解性高分子は自然環境中の微生物が有する酵素により分解を受け、低分子化することから、酵素の可逆的反応性を活用することで、高分子と低分子の間を反復する循環型ケミカルリサイクルにつなげられる。つまり、生分解性高分子の再重合性モノマー・オリゴマーへの分解と酵素触媒重合を組み合わせることでリサイクルのループが構築される。本稿では酵素としてリパーゼを用いるプラスチックリサイクル研究の現状と問題点を明らかにし、超臨界二酸化炭素流体の活用例を紹介した。

環境低負荷型触媒による合成とリサイクル技術について、ポリエステル型グリーンプラスチックの創製を重点に紹介した。なお、環境低負荷型触媒として、リパーゼおよびリパーゼに類似の挙動を示すモンモリロナイトによるポリマーの合成とケミカルリサイクル、さらに酵素を用いる超臨界二酸化炭素中の分解反応も記載した。